Polymaker PolyMax PLA Filament 1.75 mm 1 kg Black High Toughness PA02095

Standard PLA filament often fails on functional parts that need to resist impact and bending. Polymaker PolyMax PLA is engineered for high toughness and strength, making it suitable for durable prototypes, tools, and mechanical components that would otherwise crack or snap when printed in regular PLA.

Who is it for

Makers and engineers who need PLA with significantly improved impact resistance and flexural strength, without switching to more difficult materials like ABS or nylon. It prints with the ease of PLA on most desktop 3D printers.

Main features

• High toughness: Charpy impact strength of 13.2 kJ/m² and elongation at break of 14.8%
• Excellent strength: tensile strength 48.3 MPa, flexural strength 85.3 MPa
• Reliable diameter: 1.75 mm ± 0.05 mm for consistent extrusion
• 1 kg net weight spool, black colour

Specifications

• Material: PolyMax PLA
• Filament diameter: 1.75 mm
• Diameter tolerance: ± 0.05 mm
• Net weight: 1 kg
• Colour: Black
• Recommended nozzle temperature: 190 - 220 °C
• Recommended bed temperature: 25 - 60 °C
• Recommended print speed: 40 - 60 mm/s
• Density: 1.23 g/cm³
• Tensile strength: 48.3 MPa
• Elongation at break: 14.8%
• Flexural strength: 85.3 MPa
• Flexural modulus: 2496 MPa
• Impact strength (Charpy): 13.2 kJ/m²
• Heat deflection temperature (0.45 MPa): 58.6 °C
• Glass transition temperature: 61 °C
• Spool diameter: 200 mm
• Spool width: 65 mm
• Spool hub diameter: 55 mm

Tips

Store filament in a dry box to prevent moisture absorption, which can affect print quality. Use a hardened nozzle if printing frequently, as PolyMax PLA is slightly more abrasive than standard PLA.