Polymaker PolyLite LW-PLA (PA08008) - Black, 1.75mm, 0.8kg

Standard PLA can be too heavy for lightweight applications like RC aircraft and drones, where every gram counts. PolyLite LW-PLA solves this with active foaming technology that reduces weight by up to 60% compared to regular PLA, while maintaining printability and a matte finish.

Who is it for

Makers and hobbyists who need lightweight 3D printed parts, especially for RC models, drones, and cosplay props. It is also suitable for anyone looking to reduce material usage without sacrificing print quality.

Main features

• Active foaming technology expands the filament during printing, achieving a foamed density of 0.7-0.8 g/cm³.
• Up to 60% weight reduction compared to standard PLA, ideal for weight-sensitive projects.
• Matte surface finish hides layer lines and gives a professional look.
• Consistent diameter of 1.75 mm with ±0.03 mm tolerance for reliable extrusion.
• Spool made from cardboard, reducing plastic waste.

Specifications

• Material: PolyLite LW-PLA (Lightweight PLA)
• Filament Diameter: 1.75 mm
• Diameter Tolerance: ±0.03 mm
• Net Filament Weight: 0.8 kg
• Colour: Black
• Recommended Printing Temperature: 210-230 °C
• Recommended Bed Temperature: 25-60 °C (or Off)
• Foamed Density: 0.7-0.8 g/cm³
• Foaming Ratio: Up to 220% (Volume Expansion)
• Recommended Print Speed: 40-60 mm/s (for optimal foaming)
• Spool Material: Cardboard
• Spool Diameter: 200 mm
• Spool Width: 65 mm
• Spool Hub Diameter: 55 mm

Tips

For best foaming results, print at higher temperatures within the recommended range and adjust speed accordingly. Ensure proper ventilation as the foaming process may release gases. Store filament in a dry place to maintain print quality.