Polymaker Panchroma CoPE 1.75mm Black 1kg - High Toughness & Chemical Resistance Filament CA14009

With an elongation at break of 200% and notched Izod impact strength of 10 kJ/m², Polymaker Panchroma CoPE delivers exceptional toughness for functional parts that must survive real-world abuse. This black copolyester filament combines high impact resistance with excellent chemical resistance, making it a reliable choice for demanding applications.

Overview

Panchroma CoPE is a 1.75 mm filament with a diameter tolerance of ±0.03 mm, ensuring consistent extrusion and reliable prints. It is supplied on a 1 kg spool and prints at 230–250 °C with a heated bed at 80–100 °C. Recommended print speeds range from 30 to 70 mm/s with moderate cooling fan settings.

What stands out

• High toughness: 200% elongation at break and 10 kJ/m² notched Izod impact strength
• Chemical resistance for parts exposed to oils, greases, and mild solvents
• Consistent 1.75 mm diameter with ±0.03 mm tolerance
• 1 kg net weight on a standard spool (200 mm diameter, 65 mm width, 55 mm hub)

Technical details

• Material: CoPE (Copolyester)
• Density: 1.25 g/cm³
• Tensile strength: 40 MPa
• Heat deflection temperature (0.45 MPa): 60 °C
• Glass transition temperature: 70 °C
• Recommended nozzle temperature: 230–250 °C
• Recommended bed temperature: 80–100 °C
• Recommended print speed: 30–70 mm/s
• Cooling fan: Moderate

Our verdict

Polymaker Panchroma CoPE is a high-performance copolyester for users who need tough, chemically resistant parts. Its impact strength and flexibility make it ideal for functional prototypes, jigs, fixtures, and end-use components that must withstand repeated stress.