Polymaker Panchroma CoPE 1.75mm Black 1kg Filament CA14005

Polymaker Panchroma CoPE is a copolyester filament that combines high toughness with excellent layer adhesion and low warping, making it a reliable choice for printing functional parts that need to withstand impact and stress. Unlike standard PLA, CoPE offers significantly higher elongation at break, allowing printed objects to flex rather than fracture under load.

Highlights

• High toughness: Withstands impacts and bending without cracking.
• Excellent layer adhesion: Produces strong, durable prints with minimal delamination.
• Low warping: Reduces the risk of print failure on large or flat parts.
• Consistent 1.75 mm diameter with ±0.03 mm tolerance for reliable extrusion.
• Vacuum-sealed with desiccant to maintain dryness and print quality.

In daily use

Print at 230–250 °C with a bed temperature of 70–90 °C and a speed of 40–60 mm/s. The filament comes on a cardboard spool, making it easy to recycle. Its density of 1.23 g/cm³ and net weight of 1 kg provide plenty of material for multiple projects.

Full specifications

• Material: CoPE (Copolyester)
• Filament Diameter: 1.75 mm
• Diameter Tolerance: ±0.03 mm
• Net Filament Weight: 1 kg
• Color: Black
• Recommended Print Temperature: 230–250 °C
• Recommended Bed Temperature: 70–90 °C
• Recommended Print Speed: 40–60 mm/s
• Density: 1.23 g/cm³
• Tensile Strength: 45 MPa
• Elongation at Break: 250%
• Heat Deflection Temperature (HDT): 65 °C (0.45 MPa)
• Shore Hardness: D65
• Spool Material: Cardboard
• Compatibility: FDM 3D Printers

Final note

Polymaker Panchroma CoPE is a dependable filament for engineers and hobbyists who need tough, warp-resistant prints without sacrificing ease of use.