Polymaker HT-PLA (PA17006) - 1.75mm Black 1kg

Polymaker HT-PLA (PA17006) is a heat-treatable PLA filament that combines easy printing with enhanced thermal resistance after annealing. Unlike standard PLA, this filament can withstand temperatures above 100°C once annealed, making it suitable for functional parts exposed to heat.

Highlights

• Heat-treatable PLA: anneal at 80°C for 6 hours to boost heat deflection temperature from ~55°C to >100°C
• High dimensional accuracy: ±0.03 mm filament tolerance
• Eco-friendly packaging: recycled cardboard spool
• Matte surface finish for a professional look
• Compatible with most FDM 3D printers

In daily use

Print with standard PLA settings: nozzle 190-230°C, bed 25-60°C, speed 30-70 mm/s. The filament prints reliably and delivers a smooth matte finish. For heat-resistant parts, anneal after printing to unlock its full potential.

Full specifications

• Material: HTPLA (Heat Treatable PLA)
• Filament diameter: 1.75 mm
• Net weight: 1 kg
• Colour: Black
• Nozzle temperature: 190-230 °C
• Bed temperature: 25-60 °C
• Printing speed: 30-70 mm/s
• Filament tolerance: ±0.03 mm
• Heat deflection temperature (unannealed): ~55 °C
• Heat deflection temperature (annealed): >100 °C
• Tensile strength (unannealed): ~40 MPa
• Tensile strength (annealed): ~60 MPa
• Density: 1.17 - 1.24 g/cm³
• Recommended annealing: 80 °C for 6 hours
• Surface finish: Matte
• Spool material: Recycled cardboard
• Spool dimensions: 200 x 65 mm

Final note

Polymaker HT-PLA is an excellent choice for makers who need the ease of PLA with the ability to create heat-resistant parts through simple annealing.