POLMASK PA12-CF10 1.75mm Black 3kg

The POLMASK PA12-CF10 is a high-performance carbon fiber reinforced polyamide 12 (PA12) filament, designed for demanding 3D printing applications. With 10% carbon fiber content, this filament offers exceptional strength, rigidity, and temperature resistance, making it ideal for functional prototypes and end-use parts.

Advantages

This filament combines the toughness and chemical resistance of PA12 with the stiffness and dimensional stability of carbon fiber. It exhibits low shrinkage, excellent layer adhesion, and a matte black finish. The carbon fiber reinforcement significantly improves mechanical properties, including tensile strength, flexural modulus, and heat deflection temperature.

Suitable for

• Functional prototypes and end-use parts
• Jigs, fixtures, and tooling
• Automotive components
• Drone frames and parts
• Sports equipment
• Industrial applications requiring high strength and heat resistance

Key specifications

• Material: Polyamide 12 (PA12) with 10% Carbon Fiber
• Filament Diameter: 1.75 mm ± 0.03 mm
• Net Weight: 3 kg
• Colour: Black
• Recommended Print Temperature: 260-290 °C
• Recommended Bed Temperature: 90-110 °C
• Recommended Print Speed: 40-80 mm/s
• Density: 1.15 g/cm³
• Tensile Strength: 70 MPa
• Elongation at Break: 10%
• Flexural Strength: 100 MPa
• Flexural Modulus: 3000 MPa
• Heat Deflection Temperature (HDT): 150 °C (0.45 MPa)
• Impact Strength (Izod Notched): 10 kJ/m²
• Nozzle Compatibility: Hardened steel or wear-resistant nozzle recommended

Recommendations

For best results, use a hardened steel nozzle and ensure the filament is stored in a dry environment. Vacuum sealed with desiccant for optimal freshness.