Sunlu PETG High-Speed Matte Filament White 1.75mm 1kg

High-speed PETG printing with a refined matte aesthetic. Sunlu's PETG High-Speed Matte Filament delivers consistent extrusion at faster print speeds, producing robust parts with a smooth, finger-print-resistant finish. Thanks to a tight ±0.02 mm diameter tolerance, this filament guarantees reliable layer adhesion and sharp details, making it perfect for both functional prototypes and visual models.

Overview

Engineered for the modern maker, this filament blends PETG's exceptional durability with a low-glare matte surface. Each 1 kg spool is vacuum-sealed with desiccant to keep the material dry and print-ready. The 1.75 mm diameter ensures broad compatibility with most FDM 3D printers, while the high-speed formulation lets you increase throughput without compromising quality.

What stands out

• High-speed optimized: prints reliably at higher velocities, reducing production time.
• Matte finish: hides layer lines and resists fingerprints, perfect for consumer-facing parts.
• Robust mechanical properties: tensile strength ≥50 MPa and elongation at break ≥150% for impact-resistant results.
• Precise diameter: ±0.02 mm tolerance for flawless extrusion.
• Clean packaging: vacuum sealed with desiccant to prevent moisture absorption.

Technical details

• Material: PETG (Polyethylene Terephthalate Glycol)
• Filament diameter: 1.75 mm
• Diameter tolerance: ±0.02 mm
• Net weight: 1 kg
• Colour: White
• Finish: Matte
• Print temperature: 220–250 °C
• Bed temperature: 70–80 °C
• Tensile strength: ≥50 MPa
• Elongation at break: ≥150%
• Density: 1.23–1.27 g/cm³
• Melt flow index (MFI): 10–15 g/10 min (230°C, 2.16 kg)
• Spool dimensions: Ø200 × 65 mm (hub Ø56 mm)
• Compatibility: FDM 3D printers

Our verdict

Sunlu's PETG High-Speed Matte Filament is an outstanding choice for anyone seeking a balance of speed, strength, and aesthetics. Its consistent feeding and beautiful matte texture make it a go-to material for everything from engineering components to artistic displays.